Test Date: |
11/10/2006 |
|
Lab: |
Illinois
(USA) |
|
Part: |
Tube for TXRC-SC-CH-1000
(Chassis) |
|
Test Type: |
Chemical Composition /
Hardness / Strength |
|
Test Procedure: |
ASTM E415, E8
and E18.
Chemical tests to
determine composition.
Rockwell Hardness test to determine hardness.
Tensile and Yield strength. |
| |
Chassis Tubing |
|
| |
|
Test/Sample ID |
1
1/2" |
1
3/8" |
|
Carbon |
0.30% |
0.27% |
|
Manganese |
0.55 |
0.56 |
|
Sulfur |
0.012 |
0.005 |
|
Silicon |
0.25 |
0.27 |
|
Chromium |
0.96 |
0.88 |
|
Phosphorus |
0.019 |
0.010 |
|
Molybdenum |
0.16 |
0.18 |
|
Copper |
0.09 |
0.13 |
|
Nickel |
<0.05 |
<0.05 |
|
|
Rockwell Hardness
HRB(s) |
HRB 95/97 |
HRB 95 |
|
Tensile Strength
ksi |
104.2 |
95.7 |
|
Yield
Strength .2%
offset ksi |
86.8 |
85.1 |
|
Percent Elongation
in 2.0" |
15.2 |
18.1 |
|
|
Wall Thickness in
inches |
0.100 |
0.100 |
|
|
| |
|
|
|